Aluminum wire for mig welder

5183 aluminum wire for mig welder
5183 aluminum wire for mig welder is a magnesium close to 5% and higher manganese content of aluminum magnesium welding wire, with good corrosion resistance, high strength, heat resistance, good ductility. After the welding of the welding seam is still white, it can provide a good color for the welded joints. For some of the alloys, the strength of the welded joints is slightly higher than 5356 aluminum wire for mig welder.

aluminum wire for mig welder

5183 aluminum wire for mig welder
 
 
Application:
used as a filler metal for argon arc welding of aluminum magnesium (3%Mg) alloy, which is used in the locomotive, nuclear industry, shipbuilding, chemical pressure vessel, refrigeration, boiler and aerospace industry.

aluminum welding wire

5183 aluminum wire for mig welder
 
 
Physical Property
Density 
kg/dm3
Melting temperature℃ Thermal conductivity
 w/m•K
Linear expansion coefficient 
10¯6/K(20-100℃)
Electric conductivity
 % IACS
2.65 574-638 120 24.2 29
 
Weld Mechanical Properties (reference value)
Tension Strength(MPa) Yield Strength(MPa) Elongation (%)
275--300 125--140 15--20
 
ER5183 Aluminium & Aluminium Alloy welding wires
 Classification GB/T 10858-2008   AWS A5.10····       ER 5183
 
Typical composition in %
Si···················      <0.40
Fe···················     <0.40
Cu···················     <0.10
Mn·················         0.05—1.00
Mg·················         4.30—5.20
Cr·················          0.05—0.25
Zn··················          <0.25
Be··················          <0.0003
Ti··················            <0.15
Others··············                 <0.05
Others Total·········                        <0.15
 
Physical properties
(Approx.Values)
 0.2% yield strength Rpo2 (Mpa)····       125
 Tensile Strength Rm (Mpa)·····           275
Elongation A5 (L0=5d0) (%)······        17
Test Temperature (℃)······           20
 
Performance & Usage
 
This type of pwireuct is widely used in general welding material with the Mg of 
4.5%, which can be used in jointing or overlay forging and casting alloys 
processing in the same grade. Usage:pressure vessel,nuclear,ship-building,boiler,space industry ,etc .
Shielding gas Argon, Helium, or Argon/Helium—mixtures.
Dimensions Φ MIG — wires (mm):
0.8 ; 0.9 ; 1.0 ; 1.2 ; 1.6 ; 2.0 ; 2.4
TIG — wires(mm):
1.6 ; 2.0 ; 2.4 ; 3.2 ; 4.0 ; 5.0 ; 6.0
 
wire Packagings
Mig wires:
S100/0.5kg 1Lb , S200/2kg , S270-S300/6kg-7kg
Tig wire :
5/10kg     ·······     length :1000mm
 

Note:
 
1. Because of the stress corrosion cracking of the welded joint of aluminum alloy when the temperature is above 65 degrees, the electrode is not used in the structure of aluminum alloy in such a temperature environment.
 
2. Welding should be strict and clear the edge of the welding of the oxide film and oil, otherwise it will cause welding seam welding and cause the hole, slag and other defects.
 
3. Welding can be used for holding molten metal plate, in order to ensure the weld forming, and avoid hot crack.
 