Aluminum tig welding rods

5183 aluminum tig welding rods
5183 aluminum tig welding rods with a magnesium content of 5% and higher manganese content,it has good corrosion resistance, high strength, heat resistance, good ductility. After the welding of the welding seam is still white,it can provide a good color for the welded joints.For some of the alloys, the strength of the welded joints is slightly higher than 5356 aluminum tig welding rods.

aluminum tig welding rods

aluminium welding rods

Application:
used as a filler metal for argon arc welding of aluminum magnesium (3%Mg) alloy, which is used in the locomotive, chemical pressure vessel,nuclear industry, shipbuilding,  refrigeration, boiler and aerospace industry.

aluminum welding rods

5183 aluminum tig welding rods

Physical Property
Density 
kg/dm3
Melting temperature℃ Thermal conductivity
 w/m•K
Linear expansion coefficient 
10¯6/K(20-100℃)
Electric conductivity
 % IACS
2.65 574-638 120 24.2 29

Weld Mechanical Properties (reference value)
Tension Strength(MPa) Yield Strength(MPa) Elongation (%)
275--300 125--140 15--20

ER5183 Aluminium & Aluminium Alloy welding Rods
 Classification GB/T 10858-2008   AWS A5.10····       ER 5183
 
Typical composition in %
Si···················      <0.40
Fe···················     <0.40
Cu···················     <0.10
Mn·················         0.05—1.00
Mg·················         4.30—5.20
Cr·················          0.05—0.25
Zn··················          <0.25
Be··················          <0.0003
Ti··················            <0.15
Others··············                 <0.05
Others Total·········                        <0.15
 
Physical properties
(Approx.Values)
 0.2% yield strength Rpo2 (Mpa)····       125
 Tensile Strength Rm (Mpa)·····           275
Elongation A5 (L0=5d0) (%)······        17
Test Temperature (℃)······           20
 
Performance & Usage
 
This type of product is widely used in general welding material with the Mg of 
4.5%, which can be used in jointing or overlay forging and casting alloys 
processing in the same grade. Usage:pressure vessel,nuclear,ship-building,boiler,space industry ,etc .
Shielding gas Argon, Helium, or Argon/Helium—mixtures.
Dimensions Φ MIG — Rods (mm):
0.8 ; 0.9 ; 1.0 ; 1.2 ; 1.6 ; 2.0 ; 2.4
TIG — rods(mm):
1.6 ; 2.0 ; 2.4 ; 3.2 ; 4.0 ; 5.0 ; 6.0
 
Rod Packagings
Mig Rods:
S100/0.5kg 1Lb , S200/2kg , S270-S300/6kg-7kg
Tig Rod :
5/10kg     ·······     length :1000mm

Note:

1. The rod shall not be used in aluminum alloy structures where the operating temperature is greater than 65 degrees, because at this temperature the welded joint will crack and corrode. 
 
2. Welding should be strict and clear the edge of the welding of the oxide film and oil, otherwise it will cause welding seam welding and cause the hole, slag and other defects.
 
3. Welding can be used for holding molten metal plate, in order to ensure the weld forming, and avoid hot crack.