Aluminum tig welding rods

5356 aluminum tig welding rods
5356 aluminum tig welding rods is a magnesium alloy with magnesium 5% and a small amount of titanium refined aluminum alloy welding Rod, with good corrosion resistance,high strength, high heat resistance, good ductility. Weld anodizing treatment is still white,it can provide a good match for welded joints, is a widely used general consumables.

aluminum tig welding rods

aluminum welding rods

Application:
aluminum magnesium (3%Mg) alloy argon arc welding of the most basic metal filler metal, in the aluminum silicon magnesium, aluminum magnesium alloy welding and aluminum magnesium alloy castings were also used in welding. Such as the carriages,bicycles,  chemical pressure vessel, aluminum plate and other sports equipment and ordnance production, shipbuilding, aviation and other industries.

5356 aluminum tig welding rods

aluminium welding rods

Physical Property
Density 
kg/dm3
Melting temperature ℃ Thermal conductivity
 w/m•K
Linear expansion coefficient
 10¯6/K(20-100℃)
Electric conductivity
 % IACS
2.65 575-633 120 24.1 29

Weld Mechanical Properties (reference value)
Tension Strength(MPa) Yield Strength(MPa) Elongation (%)
250--300 110--140 15--25

ER5356   Aluminium & Aluminium Alloy welding Rod
 Classification GB/T 10858-2008············       HS 331
AWS A5.10··············       ER 5356
 
Typical composition in %
Si··················          <0.25
Fe··················         <0.40
Cu··················         <0.10
Mn·················        0.05—0.20
Mg···············                4.50—5.50
Cr·················         0.05—0.20
Zn··················          <0.10
Be···············                      <0.0003
Ti················              0.06—0.20
Others···············            <0.05
Others Total··········                   <0.15
 
Physical properties
(Approx.Values)
 0.2% yield strength Rpo2 (Mpa)···        110
 Tensile Strength Rm (Mpa)·····           240 Elongation A5 (L0=5d0) (%)···· 17
 Test Temperature (℃)·····               20
 
Performance & Usage
 
This type of product is widely used in general welding material with the Mg 
of 5%, which can be used in jointing or overlay forging and casting alloys 
processing. And the product is of high toughness , good forgeability, and 
well anti-comosiveness.
Shielding gas Argon, Helium, or Argon/Helium—mixtures.
Dimensions Φ MIG—Rods (mm):
0.8 ; 0.9 ; 1.0 ; 1.2 ; 1.6 ; 2.0 ; 2.4
 
TIG —rods(mm):
1.6 ; 2.0 ; 2.4 ; 3.2 ; 4.0 ; 5.0 ; 6.0
Rod Packagings  Mig Rods :
S100/0.5kg 1Lb , S200/2kg , S270-S300/6kg-7kg
Tig Rod  :
5/10kg     ·······     length :1000mm

Note :
 
1. Because of the stress corrosion cracking of the welded joint of aluminum alloy when the temperature is above 65 degrees, the electrode is not used in the structure of aluminum alloy in such a temperature environment.
 
2. Welding should be strict and clear the edge of the welding of the oxide film and oil, otherwise it will cause welding seam welding and cause the hole, slag and other defects.
 
3. Welding can be used for holding molten metal plate, in order to ensure the weld forming, and avoid hot crack.
* SEND MESSAGE *
* Product :

* Name :

* E-mail :

Phone :

Country :

* Message :

Related Products
Send Inquiry x
send inquiry
I can help you
Send